POLITEX – FUZI /APP/ | Salambo ® ADI COMMERCE LTD.

H igh-bitumen waterproofing membrane based non-woven polyester fabric, soaked and covered on both sides with bitumen modified with APP, masked by the lower side with hot melt polyethylene film with a final coating on the upper side - protective mineral layer or hot melt polyethylene film. The base of stabilized non-woven polyester fabric weighing 250 g / m² gives high resistance to mechanical deformation and dimensional stability of the product.

Polyethylene film
APP / atactic polypropylene / - modified bitumen
Reinforced base layer / glass fiber, 80 g. / M² with reinforced threads in 2 cm./
Colored mineral slate / shale / or polyethylene film

Application: waterproofing of road structures of reinforced concrete bridges, railway bridges, viaducts, road beds, parking areas, canals, tunnels, various infrastructure facilities and underground tanks.

POLITEX – FUZI

Parameters	Test Method	Measure	POLITEX FUZI
Parameters	Test Method	Measure	4,5 kg/m² without protection mineral powder	5 kg/m² without protection mineral powder	5,5 kg/m² without protection mineral powder	4.5 kg/m² with protection mineral powder	5 kg/m² with protection mineral powder	5,5 kg/m² with protection mineral powder
Type the basis	-	-	Reinforced base layer non-woven polyester fabric ≥ 250 g/m²
Type of bitumen	-	-	Modified: APP
Width	BDS ЕN 1848-1	cm	100	100	100	100	100	100
Mass per unit of area	BDS ЕN 1849-1 2004	Kg/m²	4,5	5	5,5	4,5	5	5,5
Tensile strength at break – longitudinal – cross – diagonal	BDS ЕN 12311-1: 2003	N/5cm	1010 900 1000	1100 1000 1060	1200 1000 1100	1010 900 1000	1100 1000 1060	1200 1000 1100
Elongation – longitudinal – cross – diagonal	BDS ЕN 12311-1: 2003	%	45 50 50	55 60 60	55 60 60	45 50 50	55 60 60	55 60 60
Waterproof under pressure 0,7MRa	BDS ЕN 1928:2004 Method В	-	is watertight	is watertight	is watertight	is watertight	is watertight	is watertight
Flexibility at low temperatures	BDS EN 1109:2002	°C	0 °C / minus 5 °C without changes
Heat resistance	BDS EN 1110:2005	°C	+ 120 °C no drip
Resistance of ripping off the joints – longitudinal – cross	BDS EN 12317-1: 2002	N/5cm	1030 920	1150 1005	1200 1050	1030 920	1150 1005	1200 1050
Resistance to static punching	BDS EN 12730: 2006	N	≥ 250 N	≥ 250 N	≥ 250 N	≥ 250 N	≥ 250 N	≥ 250 N
Resistance to tearing of the stem of a nail	BDS EN 12310-1: 2002	N	300	330	350	300	330	350
Shock resistance (dynamic drilling)	BDS EN 12691: 2006 Method А	-	withstand ≥ 2000 mm	withstand ≥ 2000 mm	withstand ≥ 2000 mm	withstand ≥ 2000 мм	withstand ≥ 2000 мм	withstand ≥ 2000 мм
Water Absorption	BDS 3521:1984 т. 2.6	%	0,5	0,5	0,5	0,5	0,5	0,5
Adhesion to concrete at 8⁰С	Method I-58	MPa	≥0,7	≥0,7	≥0,7	≥0,7	≥0,7	≥0,7
Content of the bitumen after extraction	BDS 3521:1984 т. 2.10.1***	%	≥ 60	≥ 60	≥ 60	≥ 60	≥ 60	≥ 60
Penetration at 25 °C	BDS 10057-83**	0,1 mm	≥ 30	≥ 30	≥ 30	≥ 30	≥ 30	≥ 30
Temperature breakage Fraas	BDS 10103-87**	°C	≤ -10	≤- 10	≤- 10	≤- 10	≤- 10	≤- 10