POLITEX – FUZI /SBS/

POLITEX FUZI - /bridge waterproofing/

H igh-bitumen waterproofing membrane based non-woven polyester fabric, soaked and covered on both sides with bitumen modified with APP, masked by the lower side with hot melt polyethylene film with a final coating on the upper side - protective mineral layer or hot melt polyethylene film. The base of stabilized non-woven polyester fabric weighing 250 g / m2 gives high resistance to mechanical deformation and dimensional stability of the product.


  • Polyethylene film
  • SBS / styrene butadiene styrene / - modified bitumen
  • Reinforced base layer non-woven polyester fabric ≥ 250 g/m2
  • Colored mineral slate / shale / or polyethylene film
Application: Waterproofing of flat roofs, pitched roofs, the second top coat for repair of old roofs, first underlay for new roofs, a second top coat for new roofs over thermal insulation.

Parameters

Test Method

Measure

POLITEX FUZI

4,5 kg/m2 without protection mineral powder

5 kg/m2 without protection mineral powder

5,5 kg/m2 without protection mineral powder

4.5 kg/m2 with protection mineral powder

5 kg/m2 with protection mineral powder

5,5 kg/m2 with protection mineral powder

Type the basis

-

-

Non-woven polyester fabric ≥ 250 gr/m2

Type of bitumen

-

-

Modified: SBS

Width

BDS ЕN 1848-1

cm

100

100

100

100

100

100

Mass per unit of area

BDS ЕN 1849-1

2004

Kg/m2

4,5

5

5,5

4,5

5

5,5

Tensile strength at break

– longitudinal

– cross

– diagonal

BDS ЕN 12311-1: 2003

N/5cm

1010

900

1000

1100

1000

1060

1200

1000

1100

1010

900

1000

1100

1000

1060

1200

1000

1100

Elongation

– longitudinal

– cross

– diagonal

BDS ЕN 12311-1: 2003

%

45

50

50

55

60

60

55

60

60

45

50

50

55

60

60

55

60

60

Waterproof under pressure 0,7MRa

BDS ЕN 1928:2004

Method В

-

impervious to water

impervious to water

impervious to water

impervious to water

impervious to water

impervious to water

Flexibility at low temperatures

BDS EN 1109:2002

°C

Depending on the order the temperature amplitude may be -10, -15, -20 °C without changes

Heat resistance

BDS EN 1110:2005

°C

+ 120 °C no drip

Resistance of ripping off the joints

– longitudinal

– cross

BDS EN 12317-1: 2002

N/5cm

1030

920

1150

1005

1200

1050

1030

920

1150

1005

1200

1050

Resistance to static punching

BDS EN 12730: 2006

N

≥ 250 N

≥ 250 N

≥ 250 N

≥ 250 N

≥ 250 N

≥ 250 N

Resistance to tearing of the stem of a nail

BDS EN 12310-1: 2002

N

300

330

350

300

330

350

Shock resistance (dynamic drilling)

BDS EN 12691: 2006 Method А

-

withstand

≥ 2000 mm

withstand

≥ 2000 mm

withstand

≥ 2000 mm

withstand

≥ 2000 mm

withstand

≥ 2000 mm

withstand

≥ 2000 mm

Water Absorption

BDS 3521:1984 т. 2.6

%

0,5

0,5

0,5

0,5

0,5

0,5

Adhesion to concrete

Method

I-58

MPa

0,7

0,7

0,7

0,7

0,7

0,7

Content of the bitumen after extraction

BDS 3521:1984 т. 2.10.1***

%

≥ 60

≥ 60

≥ 60

≥ 60

≥ 60

≥ 60

Penetration at 25 °C

BDS 10057-83**

0,1 mm

30

30

30

30

30

30

Temperature breakage Fraas

BDS 10103-87**

°C

- 15

- 15

- 15

- 15

- 15

- 15